PENGGUNAAN CARBON FIBER-REINFORCED POLYMER SEBAGAI PERKUATAN KOLOM BETON BERTULANG AKIBAT BEBAN SIKLIK UNTUK MENINGKATKAN DAKTILITAS PERPINDAHAN STRUKTUR

Abstract

The use of carbon fiber-reinforced polymer (CFRP) as a concrete column re­inforcement in order to improve the structure displacement ductility caused by a cyclic load. The aim of this research is to improve the displacement ductility of a column specimen by giving CFRP strengthener (Carbon Fiber Reinforced Polymer). Two full-scale specimens are used, C-1 (original column) and C-1C (column with CFRP strengthener 1 layer). The tests on C-1 and C-1C are respectively shown on the following results: P_max is 278.9 kN and 432.2 kN, d_max is 53.24 mm and 96.46 mm, and M_max is 328.04 kNm and 509.63 kNm. The displacement ductility of C-1 are 6.70, 6.11 and 5.44, and the displacement ductility of C-1C are 11.02, 12.75, and 11.89. The percentages of the increase of displacement ductility in column C-1C compared to C-1 are 64.48%, 108.74% and 118.68%  respectivelyfor plastic hinge zone, half high of the column effectiveness and as high as the column effectiveness.

Penelitian ini bertujuan untuk meningkatkan daktilitas perpindahan pada spe­simen kolom yang diberi perkuatan CFRP (Carbon Fiber Reinforced Polymer). Ada dua spesimen kolom skala penuh yang digunakan, yaitu C-1 (kolom original) dan C-1C (kolom dengan perkuatan CFRP 1 lapis). Hasil penelitian untuk masing-masing C-1 dan C-1C adalah P_maxsebesar 278,9 kN dan 432,2 kN, d_max sebesar 53,24 mm dan 96,46 mm, serta M_maxsebesar 328,04 kNm dan 509,63 kNm. Hasil daktilitas perpindahan untuk C-1 adalah 6,70; 6,11 dan 5,44, sedang C-1C adalah 11,02; 12,75 dan 11,89. Peningkatan persentase daktilitas per­pindahan kolom C-1C terhadap C-1 adalah 64,48%, 108,74% dan 118,68% masing-masing untuk zona sendi plastis, setengah tinggi efektif kolom dan setinggi efektif kolom.