PEMANFAATAN LIMBAH SERBUK MARMER PADA BETON SEBAGAI BAHAN PENGGANTI SEBAGIAN SEMEN DENGAN VARIASI PENGGUNAAN SILICA FUME

Abstract

The Utilization of Marble Powder Waste in Concrete Ma­­­­­­­­terials as a Partial Material Substitution of Cement  with the Variation Use of Silica Fume. The purpose of this study was to determine the effect of marble powder and silica fume on the mechanical pro­per­ties of concrete. This study used an experimental design using 16 group of testing materials with variety types of mixtures between marble powder and silica fume 0.00; 5.00; 10.00; and 15.00%. The wa­ter-cement ratio was 0.50 and a low dosage of superplasticizer, which was 0.50%. The behavior of fresh concrete were calculated and the mechanical properties of concrete were tested on con­crete age of 28 days. The results showed the marble powder main com­position was Silicon Dioxide (SiO₂) 17.63% and Calcium Carbonate (CaCO₃) 2.73%. Mar­ble powder was more appropriate to be used as fillers than to be used as a partial substitution of ce­ment. The optimum mechanical properties of concrete was produced by the mixtures of 5.00% mar­ble powder  and 6.22% silica fume which resulted in compressive strength of 29.04 MPa.

Tujuan penelitian ini adalah untuk mengetahui pengaruh peng­gunaan ser­buk marmer dan silica fume terhadap sifat mekanik beton. Penelitian ini meng­gu­na­kan desain eksperimen dengan 16 kelompok benda uji dengan variasi ser­buk marmer dan silica fume 0,00; 5,00; 10,00; dan 15,00%. Faktor air semen di­gu­nakan 0,50 dan superplasticizer dengan dosis rendah 0,50%. Perilaku beton segar di­perhitungkan dan sifat mekanik beton diuji pada umur beton 28 hari. Hasil analisis me­nunjukkan kom­posisi utama serbuk marmer adalah Silikon Dioksida (SiO₂) 17,63% dan Kalsium Kar­bonat (CaCO₃) 2,73%. Serbuk marmer lebih tepat digunakan se­bagai bahan pe­ng­isi atau filler dari pada sebagai pengganti semen. Sifat mekanik be­ton optimum di­ha­sil­kan pada campuran serbuk marmer 5,00% dan silica fume 6,22% dengan kuat tekan be­ton yang dihasilkan  mencapai 29,04 MPa.