KAJIAN EVOLUSI STRUKTUR KRISTAL DAN MAGNETODIELEKTRISITAS SENYAWA SPINTRONIK Ti1-xCoxO2+
Abstract
Abstract: One of the materials showing an excellent candidate for spintronic compounds is Ti1-xCoxO2. In order to study the compound, Ti1-xCoxO2 compound has been synthesized together with its characterization of the structure and magneto dielectric properties. Co was used as a dopant. The standard solid state reaction, X-ray, electrical capacitance measurements, and the Rietveld methods were used to synthesize material, to characterize a crystal structure, to measure the dielectric constants and to analyse the structure of materials, respectively. The results show that concentration of Co in Ti1-xCoxO2 compounds increase the crystal volume but reduce their dielectricity. However, the external magnetic field in the range of measurement reduces their dielectricity in the dopant.
Abstrak: Salah satu bahan yang menunjukkan calon yang sangat baik untuk senyawa spintronik adalah Ti1-xCoxO2. Dalam rangka mempelajari senyawa tersebut, senyawa Ti1-xCoxO2 disintesis bersamaan dengan karakterisasi stuktur dan sifat magnetodielektriknya. Co digunakan sebagai doping. Metode standar untuk reaksi fase padat, metode sinar-X, pengukuran kapasitas listrik dan metode Rietvel masing-masing digunakan untuk mensintesis bahan, mengkarakterisasi struktur kristal, mengukur konstanta dielektrik dan menganalisis struktur bahan. Hasil penelitian menunjukkan bahwa konsentrasi Co dalam senyawa Ti1-xCoxO2 meningkatkan volume kristal namun mengurangi sifat dielektrisitasnya. Namun, medan magnet eksternal di kisaran pengukuran mengurangi dielektrisitasnya dalam dopa itu.