AKTIVITAS KATALITIK TS-1 DENGAN LOKASI SISI HIDROFILIK BERBEDA: DI DALAM STRUKTUR KERANGKA DAN DI PERMUKAAN STRUKTUR KERANGKA KATALIS

Abstract

Abstract: Catalytic Activity Of TS-1 with Different Hydrophilic Sites Position: In the Framework Structure and on the Surface of Framework Structure of Catalyst. This research was aimed to study the distinction on catalytic activity between different hydrophilic sites position, which were in the framework structure and on the surface of titanium silicalite-1 (TS-1), in phenol hydroxylation with H₂O₂ as an oxidant. The catalysts used in this study were Al-TS-1 and Al₂O₃/TS-1 respectively. Al which is acid in nature was successfully increased the hydrophilic properties of the TS-1. The catalysts were then characterized using XRD, FTIR, pyridine-FTIR, and hydrophilic test techniques. Both their catalytic activities were compared also with non-modified TS-1. The result shows that the rate of hydroquinone formation increased in the following order: TS-1 > Al₂O₃/TS-1 > Al-TS-1, which had linear correlation with the hydrophilic test.

Abstrak: Aktivitas Katalitik TS-1 dengan Lokasi Sisi Hidrofilik Berbeda: di dalam Struktur Kerangka dan di Permukaan Struktur Kerangka Katalis. Penelitian ini bertujuan untuk mempelajari perbedaan kemampuan katalisis antara lokasi sisi hidrofilik di dalam dan di permukaan struktur kerangka titanium silikalit-1 (TS-1), berturut-turut adalah Al-TS-1 dan Al₂O₃/TS-1, pada reaksi hidroksilasi fenol dengan H₂O₂ sebagai oksidator. Al yang bersifat asam mampu menambah sifat hidrofilik TS-1. Katalis hasil sintesis dikarakterisasi dengan metode XRD, FTIR, FTIR-piridin, dan uji hidrofilik. Aktivitas katalitik keduanya juga dibandingkan dengan TS-1 tanpa modifikasi. Hasilnya menunjukkan bahwa kecepatan pembentukan hidroquinon sebagai produk reaksi meningkat dengan urutan: TS-1 > Al₂O₃/TS-1 > Al-TS-1, berbanding lurus dengan hasil uji hidrofilik.